National foreword

This British Standard is the UK implementation of ISO 19613:2026. It supersedes BS ISO 19613:2018, which is withdrawn.

The UK participation in its preparation was entrusted to Technical Committee RPI/13, Advanced technical ceramics.

A list of organizations represented on this committee can be obtained on request to its committee manager.

Contractual and legal considerations

This publication has been prepared in good faith, however no representation, warranty, assurance or undertaking (express or implied) is or will be made, and no responsibility or liability is or will be accepted by BSI in relation to the adequacy, accuracy, completeness or reasonableness of this publication. All and any such responsibility and liability is expressly disclaimed to the full extent permitted by the law.

This publication is provided as is, and is to be used at the recipient’s own risk.

The recipient is advised to consider seeking professional guidance with respect to its use of this publication.

This publication is not intended to constitute a contract. Users are responsible for its correct application.

Compliance with a British Standard cannot confer immunity from legal obligations.

This British Standard was published under the authority of the Standards Policy and Strategy Committee on 30 September 2026.

Foreword

ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.

The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types of ISO document should be noted. This document was drafted in accordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).

ISO draws attention to the possibility that the implementation of this document may involve the use of (a) patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a) patent(s) which may be required to implement this document. However, implementers are cautioned that this may not represent the latest information, which may be obtained from the patent database available at www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.

Any trade name used in this document is information given for the convenience of users and does not constitute an endorsement.

For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISO's adherence to the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.

This document was prepared by Technical Committee ISO/TC 206, Fine ceramics.

This second edition cancels and replaces the first edition (ISO 19613:2018), which has been technically revised.

The main changes are as follows:

clarification added to the scope;
paragraph addition in the Apparatus section on the use of different geometries;
paragraph addition in the Measurement condition on the choice of the shear rate range;
reorganisation of the Pretreatment of the sample section;
rewriting the Measurement procedure section to include the identification of the fluid behaviour.

Any feedback or questions on this document should be directed to the user’s national standards body. A complete listing of these bodies can be found at www.iso.org/members.html.

1 Scope

This document specifies a method for measurement of the viscosity of a ceramic slurry using a rotational viscometer. The method only involves rotations with a monotonic angle variation. This document does not apply to measurements using an oscillating rotation.

Ceramic slurry is used in ceramic processes such as dip coating, spray coating, screen printing, slip casting, tape casting, spray drying and polishing. This document does not apply to dispersion of fillers in molten thermoplastic polymers.

2 Normative references

3 Terms and definitions

4 Principle

4.1 Rotational viscometer with defined shear rate

4.2 Single cylinder viscometer

5 Apparatus

5.1 General

5.2 Measuring system

5.3 Single cylinder viscometer.

5.4 Temperature-control device.

6 Calibration of the rotational viscometer

7 Measurement condition

7.1 Temperature

7.2 Shear rate or angular velocity

7.3 Selection of geometry and/or spindle

8 Pretreatment of the sample

8.1 Conditioning

8.2 Mixing

8.3 Degassing

9 Measurement procedures

9.1 Sample loading

9.2 Container sealing

9.3 Determination of a flow or viscosity curve

9.4 Viscosity measurements

10 Expression of the results

11 Test report

Bibliography